Izinto zensimbi

Inkcazo emfutshane:

Umgubo wentsimbi zizinyithi ezincitshiswe zangamaqhekeza acocekileyo kwaye zizinto zokuqala ezisisiseko seenkqubo ezininzi zokuprinta i-3D ezivelisa izinto zentsimbi. 3D yoshicilelo, ekwabizwa ngokuba yimveliso eyongeziweyo (AM), kukuveliswa kwamalungu kunye neemveliso ngohlobo olwenziwe ngocingo. Zombini iimpawu zomgubo wentsimbi kunye nohlobo lwenkqubo yokuprinta ye-3D zichonga iipropathi zemveliso yokugqibela. Ukubonakala komgubo kwenzeka ngokuxhomekeke kwindlela eveliswa ngayo, enokuthi ikhokelele kwi-particle morphology kunye nococeko.

Thumela i-imeyile kuthi Khuphela njengePDF

Iinkcukacha Product

Iimpawu zemveliso

Yenziwe ngentsimbi eshayinayo, Type ； 316L
Iimpawu zomzimba	ubukhulu bamasuntswana	15-53 μm
	Imilo	Ngqukuva
	ukuhamba	I-40 S (imitha yokuhamba kweHolo)
	Ukuxinana okubonakalayo	3.9 g / cm3
	Ukuxinana	7.98 g / cm3

Ukwenziwa kweMichiza	Fe	Intsalela
	Kr	16 ～ 18 wt%
	Ni	10 ～ 14 wt%
	Mo	2, 3 wt%
	Mnu	W2 wt%
	Hayi	W1 wt%
	C	.00.05 wt%
	P	≤0.045 wt%
	S	.00.03 wt%
	O	.10.1 wt%

Iipropati zezahlulo	Ukuxinana kwesihlobo	Imilinganiselo. 99.9%
	Tensile Strength	Malunga. 560 MPa
	Unikeze Amandla	Malunga. 480 MPA
	Ukudibanisa emva kokuqhekeka	Malunga. 20%
	Imodulus yokuqina	Malunga. 180 GPa
	Ubunzima	Malunga. 85 HRB (158 HB)

IAluminiyam ingxubevange, Uhlobo: AlSi10Mg
Iimpawu zomzimba	ubukhulu bamasuntswana	15-53 μm
	Imilo	Ngqukuva
	ukuhamba	I-150 S (imitha yokuhamba kweHolo)
	Ukuxinana okubonakalayo	1.45 g / cm3
	Ukuxinana	2.67 g / cm3

Ukwenziwa kweMichiza	UAl	Intsalela
	Hayi	9 ～ 10 wt%
	Mg	0.2 ～ 0.45 wt%
	Cu	.00.05 wt%
	Mnu	0.45 wt%
	Ni	.00.05 wt%
	Fe	.50.55 wt%
	Ti	.10.15 wt%
	C	0.0075wt%

Iipropati zezahlulo	Ukuxinana kwesihlobo	≥95%
	Tensile Strength	Imilinganiselo. I-330 MPa
	Unikeze Amandla	Imilinganiselo. Ii-MPA ezingama-245
	Ukudibanisa emva kokuqhekeka	Imilinganiselo. 6%
	Imodulus yokuqina	Imilinganiselo. I-70 GPa
	Ubunzima	Imilinganiselo. I-120 HB

Ingxubevange yeTitanium, Uhlobo: TC4 (Ti-6Al-4V)
Iimpawu zomzimba	ubukhulu bamasuntswana	15-45 μm
	Imilo	Ngqukuva
	ukuhamba	I-45 S (imitha yokuhamba kweHolo)
	Ukuxinana okubonakalayo	2.5 g / cm3
	Ukuxinana	4,51 g / cm3

Ukwenziwa kweMichiza	Ti	Intsalela
	UAl	I-5 ～ 6.75 wt%
	V	3.5 ～ 4.5 wt%
	Fe	.20.25 wt%
	C	.00.02 wt%
	Y	.000.005 wt%
	O	0.14, 0.16 wt%
	N	.00.02 wt%
	Cu	.10.1 wt%
	Okunye	0.4 wt%

Iipropati zezahlulo	Ukuxinana kwesihlobo	Malunga. 99.9%
	Tensile Strength	Malunga. 2000 MPA
	Unikeze Amandla	Malunga. 900 MPa
	Ukudibanisa emva kokuqhekeka	Malunga. 10%
	Imodulus yokuqina	Malunga. 110 GPa
	Ubunzima	Malunga. 300 HV (294 HB)

Uhlobo lweNickel-base superalloy Uhlobo: IN718
Iimpawu zomzimba	ubukhulu bamasuntswana	15-53 μm
	Imilo	Ngqukuva
	ukuhamba	I-40 S (imitha yokuhamba kweHolo)
	Ukuxinana okubonakalayo	4.1 g / cm3
	Ukuxinana	8.15 g / cm3

Ukwenziwa kweMichiza	Ni	50- 55 wt%
	Kr	17 ～ 22 wt%
	Qaphela	4.75 ～ 5.5 wt%
	Mo	2.8 ～ 3.3 wt%
	Co	W1 wt%
	C	≤0.08 wt%
	P	.00.015 wt%
	Hayi	≤0.35 wt%
	UAl	0.2 ～ 0.8 wt%
	Ti	0.65 ～ 1.15 wt%
	Fe	Intsalela

Iipropati zezahlulo	Ukuxinana kwesihlobo	≥99%
	Tensile Strength	Imilinganiselo. I-980 MPa (1240 MPa emva konyango lobushushu)
	Unikeze Amandla	Imilinganiselo. I-780 MPa (i-1000 MPa emva konyango lobushushu)
	Ukudibanisa emva kokuqhekeka	12 ～ 30%
	Imodulus yokuqina	Imilinganiselo. I-160 GPa
	Ubunzima	Imilinganiselo. I-30 HRC (47 HRC emva konyango lobushushu)

Intsimbi yokuLungisa, Uhlobo: MS1
Iimpawu zomzimba	ubukhulu bamasuntswana	15-53 μm
	Imilo	Ngqukuva
	ukuhamba	I-40 S (imitha yokuhamba kweHolo)
	Ukuxinana okubonakalayo	4.3 g / cm3
	Ukuxinana	I-8 g / cm3

Ukwenziwa kweMichiza	Fe	Intsalela
	Co	I-8.5 ～ 9.5 wt%
	Ni	17 ～ 19 wt%
	Mo	4.2 ～ 5.2 wt%
	Mnu	.10.1 wt%
	Ti	0.6 ～ 0.8 wt%
	C	.00.03 wt%
	UAl	0.05 ～ 0.15 wt%
	S	.00.01 wt%
	Kr	≤0.3 wt%

Iipropati zezahlulo	Ukuxinana kwesihlobo	≥99%
	Tensile Strength	I-Arrpox. 1090 MPa (1930 MPA emva konyango lobushushu)
	Unikeze Amandla	I-Arrpox. 1000 MPa (1890 MPa emva konyango lobushushu)
	Ukudibanisa emva kokuqhekeka	I-Arrpox. 4%
	Imodulus yokuqina	I-Arrpox. 160 GPa (180 GPa emva konyango lobushushu)
	Ubunzima	I-Arrpox. 35 HRC

ICobalt-chromium alloy, Uhlobo: MP1 (CoCr-2Lc)
Iimpawu zomzimba	ubukhulu bamasuntswana	15-53 μm
	Imilo	Ngqukuva
	ukuhamba	I-40 S (imitha yokuhamba kweHolo)
	Ukuxinana okubonakalayo	4.1 g / cm3
	Ukuxinana	8.3 g / cm3

Ukwenziwa kweMichiza	Co	Intsalela
	Kr	26 ～ 30 wt%
	Mo	5 ～ 7 wt%
	Hayi	W1 wt%
	Mnu	W1 wt%
	Fe	.0.75 wt%
	C	≤0.16 wt%
	Ni	.10.1 wt%

Iipropati zezahlulo	Ukuxinana kwesihlobo	≥99%
	Tensile Strength	Malunga. 100 MPA
	Unikeze Amandla	Malunga. 900 MPa
	Ukudibanisa emva kokuqhekeka	Malunga. 10%
	Imodulus yokuqina	Malunga. 200 GPa
	Ubunzima	35 ～ 45 HRC (323 ～ 428 HB)